surewelen
Product manual
Reinforced grade 25% glass fiber reinforced material
General description
Material state Solid state
Exterior natural color
processing methods Injection molding
Stuffing glass fiber
form particle
Mechanical properties [1] Test method Test Conditions Unit Attribute value[2]
Tensile Strength ISO 527 5.0mm/min MPa 160
Elongation ISO 527 5.0mm/min % 鈮?.5
Bending strength ISO 178 2mm/min MPa 150
Flexural modulus ISO 178 2mm/min MPa 7400
Thermal performance [1] Test method Test Conditions Unit Attribute value[2]
Heat distortion temperature ISO 75/A 1.80MPa,Unannealed 掳C 215
Impact performance [1] Test method Test Conditions Unit Attribute value[2]
Izod notched impact strength ISO 180 (23卤3)掳C,Dry state kJ/m2 17
Simply supported beam unnotched impact strength ISO 179 (23卤3)掳C kJ/m2 105
Simply supported beam unnotched impact strength ISO 179 30掳C kJ/m2 75
Flammability [1] Test method Test Conditions Unit Attribute value[2]
UL flame retardant rating UL 94 1.5mm / HB
[1] The material properties of different colors will vary.
[2] The attribute values are for reference only, not as any technical indicators or technical agreements.
In the study of nylon modification, copolymer modification mainly focuses on the development of fine synthetics and high-functional products for its water absorption and processing properties. However, due to the complexity of the process, it is less used in modification. At present, PA6 raw materials with superior comprehensive performance and lower cost are mainly developed through blending and filling modification. Buy PA6
website:http://www.tlgxsales.com/plastic-raw-materials/pa6/
Reinforced grade 25% glass fiber reinforced material
General description
Material state Solid state
Exterior natural color
processing methods Injection molding
Stuffing glass fiber
form particle
Mechanical properties [1] Test method Test Conditions Unit Attribute value[2]
Tensile Strength ISO 527 5.0mm/min MPa 160
Elongation ISO 527 5.0mm/min % 鈮?.5
Bending strength ISO 178 2mm/min MPa 150
Flexural modulus ISO 178 2mm/min MPa 7400
Thermal performance [1] Test method Test Conditions Unit Attribute value[2]
Heat distortion temperature ISO 75/A 1.80MPa,Unannealed 掳C 215
Impact performance [1] Test method Test Conditions Unit Attribute value[2]
Izod notched impact strength ISO 180 (23卤3)掳C,Dry state kJ/m2 17
Simply supported beam unnotched impact strength ISO 179 (23卤3)掳C kJ/m2 105
Simply supported beam unnotched impact strength ISO 179 30掳C kJ/m2 75
Flammability [1] Test method Test Conditions Unit Attribute value[2]
UL flame retardant rating UL 94 1.5mm / HB
[1] The material properties of different colors will vary.
[2] The attribute values are for reference only, not as any technical indicators or technical agreements.
In the study of nylon modification, copolymer modification mainly focuses on the development of fine synthetics and high-functional products for its water absorption and processing properties. However, due to the complexity of the process, it is less used in modification. At present, PA6 raw materials with superior comprehensive performance and lower cost are mainly developed through blending and filling modification. Buy PA6
website:http://www.tlgxsales.com/plastic-raw-materials/pa6/